321 Датсыз корыч полоса
Датсыз корыч плиталар плитасы Баогу тәэминаты
| Тип | Сыйфат | Сыйфат | Химик компонент% | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Бүтәннәр | |||
| Остенитик | 201 | SUS201 | ≤0.15 | 16.00-18.00 | 3.50-5.50 | 5.50－7.50 | ≤0.060 | ≤0.030 | - | .001.00 | - | ≤0.25 | - |
| 202 | SUS202 | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | .001.00 | - | ≤0.25 | - | ||
| 301 | 1.431 | ≤0.15 | 16.00-18.00 | 6.00-8.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | ≤0.10 | - | |
| 304 | 1.4301 | .070.07 | 17.00-19.00 | 8.00-10.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | - | |
| 304L | 1.4307 | ≤0.030 | 18.00-20.00 | 8.00-10.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | - | |
| 304Х | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | - | |
| 309 | 1.4828 | ≤0.20 | 22.00-24.00 | 12.00-15.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | - | |
| 309С | * | .080.08 | 22.00-24.00 | 12.00-15.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | - | |
| 310 | 1.4842 | ≤0.25 | 24.00-26.00 | 19.00-22.00 | .002.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 310С | * | .080.08 | 24.00-26.00 | 19.00-22.00 | .002.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 314 | 1.4841 | ≤0.25 | 23.00-26.00 | 19.00-22.00 | .002.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | .080.08 | 16.00-18.50 | 10.00-14.00 | .002.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | .001.00 | - | - | - | |
| 316L | 1.4404 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | .002.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | .001.00 | - | - | - | |
| 316Ти | 1.4571 | .080.08 | 16.00-18.00 | 10.00-14.00 | .002.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | .001.00 | - | 0.1 | Ti5 (C + N) ~ 0.70 | |
| 317 | * | .080.08 | 18.00-20.00 | 11.00-15.00 | .002.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | .001.00 | - | 0.1 | - | |
| 317L | 1.4438 | ≤0.03 | 18.00-20.00 | 11.00-15.00 | .002.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | .001.00 | - | 0.1 | - | |
| 321 | 1.4541 | .080.08 | 17.00-19.00 | 9.00-12.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | Ti5 (C + N) ~ 0.70 | |
| 321Х | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | Ti5 (C + N) ~ 0.70 | |
| 347 | 1.455 | .080.08 | 17.00-19.00 | 9.00-12.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | Nb≥10 * C% -1.10 | |
| 347Х | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | .002.00 | ≤0.045 | ≤0.030 | - | .001.00 | - | - | Nb≥10 * C% -1.10 | |
| xm-19 | Нитроник50 | ≤0.06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | ≤0.045 | ≤0.030 | 1.50-3.00 | .001.00 | - | 0.2-0.4 | Nb: 0.10-0.30 V: 0.10-0.30 | |
| 904L | N08904 | ≤0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | ≤0.045 | ≤0.035 | .001.00 | 0.1 | Ку: 1.0-2.0 | |||
| Дуплекс | 2205 | S32205 | ≤0.03 | 22.0-23.0 | 4.5-6.5 | .002.00 | ≤0.030 | ≤0.020 | 3.0-3.5 | .001.00 | - | 0.14-0.20 | |
| 2507 | S32750 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.20 | ≤0.035 | ≤0.020 | 3.0-5.0 | ≤0.80 | 0,5 | 0.24-0.32 | ||
| * | S32760 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | .001.00 | ≤0.030 | ≤0.010 | 3.0-4.0 | .001.00 | 0.5-1.00 | 0.2-0.3 | ||
| 2304 | S32304 | ≤0.03 | 21.5-24.5 | 3.0-5.5 | ≤2.50 | ≤0.040 | ≤0.030 | 0.05-0.6 | .001.00 | 0.05-0.6 | 0.05-0.2 | ||
| 329 | 1.446 | .080.08 | 23.00-28.00 | 2.00-5.00 | .001.00 | ≤0.040 | ≤0.030 | 1.00-2.00 | ≤0.75 | - | - | ||
| Феррит | 409 | S40900 | ≤0.03 | 10.50-11.70 | 0,5 | .001.00 | ≤0.040 | ≤0.020 | - | .001.00 | - | ≤0.030 | Ti6 (C + N) ~ 0.50 Nb: 0.17 |
| 430 | 1Кр17 | ≤0.12 | 16.00-18.00 | - | .011.0 | ≤0.040 | ≤0.030 | - | .011.0 | - | - | - | |
| 444 | S44400 | ≤0.025 | 17.50-19.50 | 1 | .001.00 | ≤0.040 | ≤0.030 | 1.75-2.5 | .001.00 | - | 0.035 | Ti + Nb: 0,2 + 4 (C + N) ~ 0.80 | |
| 446 | S44600 | ≤0.20 | 23.00-27.00 | 0.75 | .51.5 | ≤0.040 | ≤0.030 | 1.50-2.50 | .001.00 | - | ≤0.25 | - | |
| Мартенсит | 410 | 1Кр13 | 0.08-0.15 | 11.50-13.50 | 0.75 | .001.00 | ≤0.040 | ≤0.030 | - | .001.00 | - | - | - |
| 410С | * | ≤0.080 | 11.50-13.50 | 0.6 | .001.00 | ≤0.040 | ≤0.030 | - | .001.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0.15 | 12.00-14.00 | 3) | ≤1.25 | ≤0.060 | ≥0.15 | - | .001.00 | - | - | - | |
| 420 | 2Кр13 | ≥0.15 | 12.00-14.00 | - | .001.00 | ≤0.040 | ≤0.030 | - | .001.00 | - | - | - | |
| 420J2 | 3Кр13 | 0.26-0.35 | 12.00-14.00 | - | .001.00 | ≤0.040 | ≤0.030 | - | .001.00 | - | - | - | |
| 431 | 1Кр17Ни2 | ≤0.20 | 15.00-17.00 | 1.50-2.50 | .001.00 | ≤0.040 | ≤0.030 | - | ≤0.80 | - | - | - | |
| 440С | 11Кр17 | 0.95-1.20 | 16.00-18.00 | - | .001.00 | ≤0.040 | ≤0.030 | 0.75 | .001.00 | - | - | - | |
| PH | 630 | 17-4PH | .070.07 | 15.00-17.50 | 3.00-5.00 | .001.00 | ≤0.035 | ≤0.030 | - | .001.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
| 631 | 17-7PH | ≤0.09 | 16.00-18.00 | 6.50-7.50 | .001.00 | ≤0.035 | ≤0.030 | - | .001.00 | ≤0.50 | - | Al 0.75-1.50 | |
| 632 | 15-5PH | ≤0.09 | 14.00-16.00 | 3.50-5.50 | .001.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | .001.00 | 2.5-4.5 | - | Al 0.75-1.50 | |
Тасвирлау
321 дат басмас корыч полоса - аз углеродлы һәм күп коррозицион мохиттә яхшы коррозиягә каршы торучы остенитик датсыз корычның бер төре.321 искиткеч эретеп ябыштыру, яхшы эшкәртүчәнлек һәм искиткеч ясалма үзенчәлекләр тәкъдим итә.
321 дат басмаган корыч полоса гадәттә химия сәнәгатендә, су һәм кәгазь сәнәгатендә, диңгез һәм диңгез инженерия сәнәгатендә, шулай ук азык-төлек һәм эчемлек сәнәгатендә кулланыла.
321 дат басмаган корыч полоса шулай ук хлорид стресс коррозиясенең ярылуына һәм чокырына каршы торуның югары дәрәҗәсенә ия.Ул шулай ук 250 ° C (480 ° F) кадәр күтәрелгән температурада гидрохлор кислотасына чыдам.
Үзенчәлекләр
Яхшы коррозиягә каршы тору: 321 дат басмас корыч полоса коррозиягә каршы торуга 304 һәм 316 төргә караганда яхшырак коррозиягә ия, бу аны коррозицион шартларда куллану өчен идеаль итә.
Искиткеч эретеп ябыштыру: 321 дат басмас корыч полосаны барлык ысуллар белән эретеп ябыштырырга мөмкин (TIG / GTAW), электрон нур белән эретеп ябыштыру (EBW / EFW), су асты дугасы эретү (SAW) һәм лазер нурлары белән эретү (LBIW).
Stгары көч: 321 дат басмас корыч полосаның көч дәрәҗәсе 304 төр басмас корычныкыннан 50% ка, углерод күләме һәм остенит ашлык күләме аркасында 316 төр басмас корычныкыннан 80% ка югарырак.